vzorekC1_poz1
vzorekC1_poz1
Indentation # 1
Indentation parameters
+ Standard + NHTX S/N: 01-03880 settings
Acquisition Rate : 10.0 [Hz] Approach distance : 3000 nm
Linear Loading Approach speed : 2000 nm/min
Max load : 245.00 mN Retract speed : 2000 nm/min Loading rate : 490.00 mN/min Dz sensor in fine range
Unloading rate : 490.00 mN/min Stiffness Threshold : 400 µN/µm
Pause : 15.0 s Date : 3/16/2016
Hour : 1:31:02 PM
Indenters
Type : Berkovich
Serial number : BL 25 FS 03.02.2014 Material : Diamond
Curves
250.0 225.0
200.0
175.0
150.0
125.0
100.0
75.0
50.0
25.0 0.0 mN
5000.0 4500.0
4000.0
3500.0
3000.0
2500.0
2000.0
1500.0
1000.0
500.0
0.0 nm Penetration depth Normal force
1 vzorekC1_poz1 - 3/16/2016
250.0 225.0 200.0 175.0 150.0 125.0 100.0 75.0 50.0
25.0 0.0 mN
0.0 nm 500.0 1000.0 1500.0 2000.0 2500.0 3000.0 3500.0 4000.0 4500.0 5000.0
Indentation
2 vzorekC1_poz1 - 3/16/2016
Indentation # 2
Indentation parameters
+ Standard + NHTX S/N: 01-03880 settings
Acquisition Rate : 10.0 [Hz] Approach distance : 3000 nm
Linear Loading Approach speed : 2000 nm/min
Max load : 245.00 mN Retract speed : 2000 nm/min Loading rate : 490.00 mN/min Dz sensor in fine range
Unloading rate : 490.00 mN/min Stiffness Threshold : 400 µN/µm
Pause : 15.0 s Date : 3/16/2016
Hour : 1:35:54 PM
Indenters
Type : Berkovich
Serial number : BL 25 FS 03.02.2014 Material : Diamond
Curves
250.0 225.0
200.0
175.0
150.0
125.0
100.0
75.0
50.0
25.0 0.0 mN
5000.0 4500.0
4000.0
3500.0
3000.0
2500.0
2000.0
1500.0
1000.0
500.0
0.0 nm Penetration depth Normal force
3 vzorekC1_poz1 - 3/16/2016
250.0 225.0 200.0 175.0 150.0 125.0 100.0 75.0 50.0
25.0 0.0 mN
0.0 nm 500.0 1000.0 1500.0 2000.0 2500.0 3000.0 3500.0 4000.0 4500.0 5000.0
Indentation
4 vzorekC1_poz1 - 3/16/2016
Indentation # 3
Indentation parameters
+ Standard + NHTX S/N: 01-03880 settings
Acquisition Rate : 10.0 [Hz] Approach distance : 3000 nm
Linear Loading Approach speed : 2000 nm/min
Max load : 245.00 mN Retract speed : 2000 nm/min Loading rate : 490.00 mN/min Dz sensor in fine range
Unloading rate : 490.00 mN/min Stiffness Threshold : 400 µN/µm
Pause : 15.0 s Date : 3/16/2016
Hour : 1:40:21 PM
Indenters
Type : Berkovich
Serial number : BL 25 FS 03.02.2014 Material : Diamond
Curves
250.0 225.0
200.0
175.0
150.0
125.0
100.0
75.0
50.0
25.0 0.0 mN
5000.0 4500.0
4000.0
3500.0
3000.0
2500.0
2000.0
1500.0
1000.0
500.0
0.0 nm Penetration depth Normal force
5 vzorekC1_poz1 - 3/16/2016
250.0 225.0 200.0 175.0 150.0 125.0 100.0 75.0 50.0
25.0 0.0 mN
0.0 nm 500.0 1000.0 1500.0 2000.0 2500.0 3000.0 3500.0 4000.0 4500.0 5000.0
Indentation
6 vzorekC1_poz1 - 3/16/2016
Indentation # 4
Indentation parameters
+ Standard + NHTX S/N: 01-03880 settings
Acquisition Rate : 10.0 [Hz] Approach distance : 3000 nm
Linear Loading Approach speed : 2000 nm/min
Max load : 245.00 mN Retract speed : 2000 nm/min Loading rate : 490.00 mN/min Dz sensor in fine range
Unloading rate : 490.00 mN/min Stiffness Threshold : 400 µN/µm
Pause : 15.0 s Date : 3/16/2016
Hour : 1:44:20 PM
Indenters
Type : Berkovich
Serial number : BL 25 FS 03.02.2014 Material : Diamond
Curves
250.0 225.0
200.0
175.0
150.0
125.0
100.0
75.0
50.0
25.0 0.0 mN
5000.0 4500.0
4000.0
3500.0
3000.0
2500.0
2000.0
1500.0
1000.0
500.0
0.0 nm Penetration depth Normal force
7 vzorekC1_poz1 - 3/16/2016
250.0 225.0 200.0 175.0 150.0 125.0 100.0 75.0 50.0
25.0 0.0 mN
0.0 nm 500.0 1000.0 1500.0 2000.0 2500.0 3000.0 3500.0 4000.0 4500.0 5000.0
Indentation
8 vzorekC1_poz1 - 3/16/2016
Indentation # 5
Indentation parameters
+ Standard + NHTX S/N: 01-03880 settings
Acquisition Rate : 10.0 [Hz] Approach distance : 3000 nm
Linear Loading Approach speed : 2000 nm/min
Max load : 245.00 mN Retract speed : 2000 nm/min Loading rate : 490.00 mN/min Dz sensor in fine range
Unloading rate : 490.00 mN/min Stiffness Threshold : 400 µN/µm
Pause : 15.0 s Date : 3/16/2016
Hour : 1:48:23 PM
Indenters
Type : Berkovich
Serial number : BL 25 FS 03.02.2014 Material : Diamond
Curves
250.0 225.0
200.0
175.0
150.0
125.0
100.0
75.0
50.0
25.0 0.0 mN
3000.0 2700.0
2400.0
2100.0
1800.0
1500.0
1200.0
900.0
600.0
300.0
0.0 nm Penetration depth Normal force
9 vzorekC1_poz1 - 3/16/2016
250.0 225.0 200.0 175.0 150.0 125.0 100.0 75.0 50.0
25.0 0.0 mN
0.0 nm 300.0 600.0 900.0 1200.0 1500.0 1800.0 2100.0 2400.0 2700.0 3000.0
Indentation
10 vzorekC1_poz1 - 3/16/2016
Statistic
New Report
HIT (O&P) [MPa]
HVIT (O&P) [Vickers]
EIT (O&P) [GPa]
Data : 1 Data : 2 Data : 3 Data : 4 Data : 5 Mean Std Dev Median Data : 1 Data : 2 Data : 3 Data : 4 Data : 5 Mean Std Dev Median Data : 1 Data : 2 Data : 3 Data : 4 Data : 5 Mean Std Dev Median
vzorekC1_poz1 550.778
596.692 591.171 675.219 1760.694 834.911 519.487 596.692 51.008 55.260 54.749 62.533 163.059 77.322 48.110 55.260 16.347 17.432 16.452 17.058 35.548 20.567 8.386 17.058
11 vzorekC1_poz1 - 3/16/2016
12 vzorekC1_poz1 - 3/16/2016
vzorekC1_poz1 - 1 - Fn [mN]
vzorekC1_poz1 - 2 - Fn [mN]
vzorekC1_poz1 - 3 - Fn [mN]
vzorekC1_poz1 - 4 - Fn [mN]
vzorekC1_poz1 - 5 - Fn [mN]
13 vzorekC1_poz1 - 3/16/2016