vzorekC3_poz5
vzorekC3_poz5
Indentation # 1
Indentation parameters
+ Advanced + NHTX S/N: 01-03880 settings
Acquisition Rate : 10.0 [Hz] Approach distance : 3000 nm
Linear Loading Approach speed : 2000 nm/min
Max load : 245.00 mN Retract speed : 2000 nm/min Loading rate : 490.00 mN/min Dz sensor in fine range
Unloading rate : 490.00 mN/min Stiffness Threshold : 500 µN/µm
Pause : 15.0 s Date : 1/7/2016
Hour : 11:00:55 AM
Indenters
Type : Berkovich
Serial number : BL 25 FS 03.02.2014 Material : Diamond
Curves
250.0 225.0
200.0
175.0
150.0
125.0
100.0
75.0
50.0
25.0 0.0 mN
4000.0 3600.0
3200.0
2800.0
2400.0
2000.0
1600.0
1200.0
800.0
400.0
0.0 nm Penetration depth Normal force
1 vzorekC3_poz5 - 1/7/2016
250.0 225.0 200.0 175.0 150.0 125.0 100.0 75.0 50.0
25.0 0.0 mN
0.0 nm 400.0 800.0 1200.0 1600.0 2000.0 2400.0 2800.0 3200.0 3600.0 4000.0
Indentation
Indentation # 2
Indentation parameters
+ Advanced + NHTX S/N: 01-03880 settings
Acquisition Rate : 10.0 [Hz] Approach distance : 3000 nm
Linear Loading Approach speed : 2000 nm/min
Max load : 245.00 mN Retract speed : 2000 nm/min Loading rate : 490.00 mN/min Dz sensor in fine range
Unloading rate : 490.00 mN/min Stiffness Threshold : 500 µN/µm
Pause : 15.0 s Date : 1/7/2016
Hour : 11:05:57 AM
Indenters
Type : Berkovich
Serial number : BL 25 FS 03.02.2014 Material : Diamond
Curves
250.0 225.0
200.0
175.0
150.0
125.0
100.0
75.0
50.0
25.0 0.0 mN
2500.0 2250.0
2000.0
1750.0
1500.0
1250.0
1000.0
750.0
500.0
250.0
0.0 nm Penetration depth Normal force
3 vzorekC3_poz5 - 1/7/2016
250.0 225.0 200.0 175.0 150.0 125.0 100.0 75.0 50.0
25.0 0.0 mN
0.0 nm 250.0 500.0 750.0 1000.0 1250.0 1500.0 1750.0 2000.0 2250.0 2500.0
Indentation
Statistic
New Report
HIT (O&P) [MPa]
HVIT (O&P) [Vickers]
EIT (O&P) [GPa]
Data : 1 Data : 2 Mean Std Dev Median Data : 1 Data : 2 Mean Std Dev Median Data : 1 Data : 2 Mean Std Dev Median
vzorekC3_poz5 1376.641 2502.458 1939.550 796.073 1376.641 127.492 231.755 179.623 73.725 127.492 36.056 50.096 43.076 9.928 36.056
5 vzorekC3_poz5 - 1/7/2016
vzorekC3_poz5 - 1 - Fn [mN]
vzorekC3_poz5 - 2 - Fn [mN]
7 vzorekC3_poz5 - 1/7/2016